Discontinued - Permabond TA4660 Nylon Bonding MMA Acrylic Adhesive – 50 ml
Need Datasheets?
Click Here to visit our Datasheet Server (TDS, SDS, Fact Sheets, Selector Guides, etc)This formula has been discontinued. It has been replaced by the Permabond TA4550, which is a new formulation, and a very close substitute for features and use cases.
Link to: Permabond TA4550
PERMABOND TA4660 was a 2-part, 2:1 low odor, acrylic adhesive. It was developed for the structural bonding of nylon/polyamide (filled and unfilled) without the need for any primers or additional surface treatment, such as plasma. TA4660 was also good for bonding nylon in combination with certain metals. It cured at room temperature and contained microbeads to control the bond line thickness for superior performance.
Features & Benefits
- Excellent adhesion to nylon
- No primers required
- Full cure at room temperature
- Low odor
- Good temperature resistance
Surfaces it bonded to: Nylon, Polyamides, Carbon Steel, Stainless Steel, Aluminum, Most other Metals, Wood, Ceramics, Rock, Concrete, Glass, Fiberglass
Physical Properties of Uncured Adhesive
| TA4660 A | TA4660 B | |
| Chemical Composition | Methacrylate | Methacrylate |
| Color | Yellow | Black |
| Mixed Color | Dark green/grey | |
| Viscosity @ 25°C | 100,000 mPa.s (cP) Thixo paste | 100,000 mPa.s (cP) |
| Specific gravity | 1.0 | 1.0 |
Typical Curing Properties
| Ratio to Use | 2: 1 |
| Maximum gap fill (NB: Contains microparticles to control gap) | 1 mm (0.04 in) |
| Pot life (2g+2g) @23°C | 5 minutes |
| Fixture time (0.1 N/mm² shear strength is achieved) @23°C | 25 minutes |
| Handling time (0.3 N/mm² shear strength is achieved) @23°C | 90 minutes |
| Working strength @23°C | 2 hours |
| Full cure @23°C | 48 hours |